烧结工艺对液相合成（SrPb）TiO3基陶瓷热敏特性影响的研究

本文在液相合成（ＳｒＰｂ）ＴｉＯ３粉的基础上，研究了升温速率、保温时间、烧结温度及降温方式对（ＳｒＰｂ）ＴｉＯ３基陶瓷的Ｖ型ＰＴＣ热敏特性的影响。实验表明：升温速率对其热敏特性影响不大，保温时间和烧结温度的作用是一致的，具有一最佳范围。而降浊方式对材料的热敏特性影响较大。综合各因素的影响，本配方中，样品的烧结制度定为：以２００℃／ｈ的速率升温，在１２５０℃保温１ｈ，炉冷至９５０℃，保温０．５ｈ，再     

LD钢超塑性压缩变形参数与金相组织

通过对ＬＤ（７Ｃｒ７Ｍｏ３Ｖ２Ｓｉ）模具钢起塑性压缩变形后的金相组织观察研究，分析了变形参数、原始组织对变形后金相组织的影响。     

Breakdown characteristics of oil and paper insulation for a very fast transient voltage

This paper describes the dielectric breakdown characteristics of oil and oil‐impregnated paper for very fast transient (VFT) voltages. Blumlein circuits generate VFT voltages of 60 and 300 ns in a pulse width that simulates disconnecting switching surges in gas‐insulated switch gears. We measured the breakdown voltages of needle‐to‐plane, plane‐to‐plane oil gaps and several pieces of paper between plane electrodes for VFT and lightning impulse voltages. The measured data were formulated in V‐t characteristics and Weibull probability distributions. The inclination n of V‐t characteristics of insulating paper is 150, which is less than n = 13.7 of the plane‐to‐plane oil gap in the VFT time range. The shape parameters of Weibull distribution obtained in this study show that the scattering of breakdown voltages of paper is much less than that of oil. © 2002 Wiley Periodicals, Inc. Electr Eng Jpn, 141(4): 16–24, 2002; Published online in Wiley InterScience ( www.interscience.wiley.com ). DOI 10.1002/eej.10043     

David V. Smith (1943-2006).

Presents an obituary for David V. Smith, who succumbed to a brain tumor on September 30, 2006 at the age of 63. He was Simon R. Bruesch Professor and chair of the Department of Anatomy and Neurobiology and the director of the Neuroscience Institute at the University of Tennessee Health Science Center (UTHSC). (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

高速钢W6Mo5Cr4V2的脱磷试验

在３０ｋｇ感应炉上用ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ（ＭｏＯ３）渣、ＭｏＣｌ６粉剂和Ａｌ－Ｃａ合金作脱磷剂对高速钢Ｗ６Ｍｏ５Ｃｒ４Ｖ２进行脱磷试验。结果表明，ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ渣的脱磷效果最好，一般脱磷率可达２６％￣５６％。     

p,V, T and derived thermodynamic data for toluene,trichloromethane, dichloromethane,acetonitrile, aniline,and n-dodecane

Experimentally determined p,V,T data are reported for toluene, trichloromethane, dichloromethane, acetonitrile, aniline, and n-dodecane at 278, 288, 298, 313, and 323 K, except for dichloromethane, for which the highest temperature was 298 K. At each temperature, measurements were done at pressures up to about 280 MPa or (for aniline and n-dodecane) at a lower pressure slightly below the freezing pressure at the temperature of measurement. Values of the isobaric expansivity isothermal compressibility and (for toluene, trichloromethane, dichloromethane, and acetonitrile) internal pressure, derived from the p,V,T data, are presented.     

Influence of Ni Interlayers on the Mechanical Properties of Ti6Al4V/(WC-Co) Friction Welds

Ni interlayers were introduced prior to dissimilar friction welding of Ti6Al4V base material to three cemented carbide substrates. The fracture strength of Ti6Al4V/(WC-6 wt% Co) welds were poor and were markedly improved when 20-µm thick Ni interlayers were introduced prior to dissimilar friction welding. These results were only produced when the (WC-6 wt% Co) cermet was electroplated prior to friction welding. When the Ti6Al4V alloy was electroplated prior to friction welding, fractured WC particles and cracking were observed in the (WC-Co) carbide substrate. The fracture strengths of Ti6Al4V/(WC-11 wt% Co) and Ti6Al4V/(WC-24 wt% Co) welds were not improved when 20-µm thick Ni interlayers were introduced prior to friction welding. During mechanical testing, the Ni layer retained at the dissimilar joint interface created a region of weakness.     

Surface structural change of ZnO-coated LiNi0.5Mn1.5O4 spinel as 5 V cathode materials at elevated temperatures

LiNi_0.5Mn_1.5O₄ powder was synthesized via sol-gel method and coated with ZnO in order to test the electrochemical cyclability of the material as a cathode for the secondary Li battery in the 5 V range at 55 °C. The ZnO-coated LiNi_0.5Mn_1.5O₄ powder nearly maintained its initial capacity of 137 mA h g⁻¹ after 50 cycles whereas the uncoated powder was able to retain no more than 10% of the initial capacity after 30 cycles. TEM analysis of the cycled cathodes suggests that the formation of the graphitic surface phase, hindering the Li migration, may be responsible for the rapid capacity loss of the uncoated material while no such phase was observed on the surface of the ZnO coated LiNi_0.5Mn_1.5O₄ powder.     

P、V操作的新探讨

P、V操作的概念以及使用在操作系统中非常重要、这里从一些新颖的角度来分析P、V操作，用P、V操作来实现进程的同步与互斥以及一种简单易行的逻辑关系则可以解决P操作嵌套时的执行次序。     

轴端沟槽底部激光强化工艺参数优化研究

分析了选用不同激光能量密度对HT300进行表面强化处理时，材料表面呈现的四种状况；未相变硬化、相变硬化、表面微熔与表面熔凝的金相组织。根据工艺要求，选取相变硬化方法对轴端沟槽底表面进行处理。分析了工件激光处理方法并通过试验研究，寻找轴端沟槽底部激光强化工艺参数；激光功率（P）、光斑直径（D）及扫描速度（V）的优化组合。硬度测试及耐磨性能试验表明：激光相变处理和激光熔凝处理后轴端沟槽底部表面较表面感应淬火硬度分别提高7%和34%，绝对磨损体积分别下降了13%和25%。实践证实，对轴端沟槽底部激光相变硬化处理方法较其他表面处理方法工艺简单，加工工件符合技术要求，试验结果对零件表面处理提供了可靠依据。