Magnetic recyclable ZnO/SrFe12O19 photocatalyst for effective photodegradation of rhodamine B under simulated sunlight

This work develops a novel magnetic photocatalysts ZnO/SrFe₁₂O₁₉ (ZS) synthesized with hydrothermal process. The introduction of SrFe₁₂O₁₉ not only enhances the photocatalytic behavior of ZnO towards Rhodamine B (RhB) decomposition, but also reinforces the recycling stability. Especially, ZS-5 composite exhibits the optimal photocatalytic performance, and the RhB decomposition reaches 99.5% after being exposed to simulative sunlight for 70 min, which is obviously superior to that of bare ZnO. Furthermore, the ZS-5 can be recovered from RhB solution by an extra magnet space and reused. After five recycles, the RhB removal efficiency can still be maintained over 90%. Such prominent photocatalytic property and stability of ZS-5 are associated with the greatly improved detachment efficiency of photoexcited carriers in a magnetic field. This study could provide a new-type recyclable photocatalyst that can effectively purify dye wastewater for convenient recovery.     

Magnetic properties,phase evolution,hollow structure and biomedical application of hematite (α-Fe2O3) and QUAIPH

We investigate synthesis, phase evolution, hollow and porous structure and magnetic properties of quasi-amorphous intermediate phase (QUAIPH) and hematite (α-Fe₂O₃) nanostructure synthesized by annealing of akaganeite (β-FeOOH) nanorods. It is found that the annealing temperature determines the phase composition of the products, the crystal structure/size dictates the magnetic properties whereas the final nanorod morphology is determined by the starting material. Annealing of β-FeOOH at ～300 °C resulted in the formation of hollow QUAIPH nanorods. The synthesized material shows low-cytotoxicity, superparamagnetism and good transverse relaxivity, which is rarely reported for QUAIPH. The QUAIPH nanorods started to transform to porous hematite nanostructures at ～350 °C and phase transformation was completed at 600 °C. During the annealing, the crystal structure changed from monoclinic (akaganeite) to quasi-amorphous and rhombohedral (hematite). Unusually, the crystallite size first decreased (akaganeite → QUAIPH) and then increased (QUAIPH → hematite) during annealing whereas the nanorods retained particle shape. The magnetic properties of the samples changed from antiferromagnetic (akaganeite) to superparamagnetic with blocking temperature T_B = 84 K (QUAIPH) and finally to weak-ferromagnetic with the Morin transition at T_M = 244 K and high coercivity H_C = 1652 Oe (hematite). The low-cytotoxicity and MRI relaxivity (r₂ = 5.80 mM^?1 s^?1 (akaganeite), r₂ = 4.31 mM^?1 s^?1 (QUAIPH) and r₂ = 5.17 mM^?1 s^?1 (hematite)) reveal potential for biomedical applications.     

The structure,vacancy characteristics,and magnetic properties of GdMn1-xCrxO3 ceramics

To investigate the evolution of the structural and enhanced magnetic properties of GdMnO₃ systems induced by the substitution of Mn with Cr, polycrystalline GdMn_1-xCr_xO₃ samples were synthesized via solid-state reactions. XRD characterization shows that all GdMn_1-xCr_xO₃ compounds with single-phase structures crystallize well and that Cr³⁺ ions entering the lattice sites of GdMnO₃ induce structural distortion. SEM results indicate that the grain size of the synthesized samples (a few microns) decreases as the Cr substitution concentration increases. Positron annihilation lifetime spectroscopy reveals that vacancy-type defects occur in GdMn_1-xCr_xO₃ ceramics and that the vacancy size and concentration clearly change with the Cr content. The temperature and field dependence of the magnetization curves show that Cr substitution significantly influences the magnetic ordering of the gadolinium sublattice, improving the weak ferromagnetic transition temperature and magnetization of GdMn_1-xCr_xO₃. The enhanced magnetization of GdMn_1-xCr_xO₃ is closely related to the vacancy defect concentration.     

Transport properties in spinel ferrite/graphene oxide nanocomposites for electromagnetic shielding

Herein, $\left({\text{Co}}_{0.5}{\text{Ni}}_{0.5}\right){\text{Cr}}_{0.3}{\text{Fe}}_{1.7}{\text{O}}_4$/graphene oxide nanocomposites were fabricated by ultrasonication technique, using pure spinel ferrite and graphene oxide synthesized by sol-gel method and modified Hummers' method, respectively. The effect of graphene incorporation with ferrite nanoparticles was studied by X-ray diffraction (XRD), electrical and dielectric measurements. XRD analysis revealed the spinel phase for the ferrite sample and confirmed the formation of graphene oxide. The crystallite size was found in the range of $37-43\text{ nm}$ and the porosity increased with the increase in the concentration of graphene oxide in the composites. The DC electrical resistivity of spinel ferrite was found equal to $3.83\times {10}^9\text{ Ω}.\text{cm}$ and it substantially decreased with the increase in the percentage of graphene oxide at room temperature. The real and imaginary part of relative permittivity followed the Maxwell-Wagner type of interfacial polarization. AC conductivity confirmed the conduction by hopping mechanism and increased on increasing the GO content. The coupling of magnetic ferrite with graphene oxide tunes the magneto-electrical properties for potential applications at high frequencies.     

Magnetic field-enhanced photocatalytic nitrogen fixation over defect-rich ferroelectric Bi2WO6

Photocatalytic N₂ fixation is a promising and sustainable manufacturing process of ammonia (NH₃); however, the NH₃ production rate by this method is very low, thus severely restricting further application of this sustainable technology. Therefore, developing an efficient photocatalyst for N₂ fixation under mild conditions is urgently required. Herein, ferroelectric Bi₂WO₆ materials with different surface oxygen defects were prepared, and the concentration of corresponding defects was controlled by adjusting the thermal reduction time. The abundant oxygen defects in Bi₂WO₆ can provide more reactive sites to promote the effective adsorption of N₂, and the photogenerated charge carrier can be efficiently separated benefiting from the internal electric field. These would weaken the N₂ triple bond and reduce the activation energy barrier for the conversion of N₂ to NH₃ under mild conditions. In the absence of sacrificial agents and cocatalysts, the optimized Bi₂WO₆ with oxygen defects shows an indigenous NH₃ yield of 132.175 μmol·g^-1·L^-1·h^-1, which is more than two times higher than that of the original Bi₂WO₆. Surprisingly, the Bi₂WO₆ with oxygen defects produced more than eight times NH₃ (471.13 μmol·g^-1·L^-1·h^-1) than that of the original Bi₂WO₆ when assisted by an external magnetic field, thus providing a new perspective for further enhancing the N₂ fixation performance.     

深孔爆破成井技术在三道庄钼矿的试验与应用研究

洛钼集团矿山公司三道庄矿区由于历史原因,露天开采境界地下内存在的采空区已危及矿山公司的正常安全生产,阻碍了洛钼集团可持续发展。为解决这一重大问题,经过充分调研和多方论证,认为深孔一次爆破成井技术是解决此类采空区难题唯一的经济上合理、技术可行、安全可靠的手段与途径。深孔爆破成井实现与采空区顶板的贯通,使采空区边岩稳定,顶岩暴露面积缩小,确保了采空区的稳定;保证了台阶正常推进。     

Anisotropic thermal expansion and ionic conductivity of a crystal-oriented,Mg2+-conducting NASICON-type solid electrolyte

Multivalent ion-conducting ceramics are required for the manufacture of high-safety, high-capacity rechargeable batteries. However, the low ionic conductivity of solid electrolytes and discrepancies in the thermal expansion between the battery components limit their widespread application. Furthermore, anisotropic thermal expansion in crystals during battery manufacturing and the charge-discharge cycles causes the formation of microcracks, which degrade the battery performance. The physical properties of ceramic materials with anisotropic crystal structures can be modified by varying the crystallographic orientation of their grains. In this study, a co-precipitation approach was used to synthesize an Mg²⁺-conducting (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ solid electrolyte, and the grain orientation in the bulk sample was controlled using strong magnetic fields during the slip casting process. The results showed that inducing an orientation along the c-axis enhanced the apparent ionic conductivity of the bulk sample. It was also observed that (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ crystal has a negative volumetric thermal expansion despite a positive linear thermal expansion along its c-axis. By adjusting the c-axis orientation of the grains, (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ electrolytes with negative or positive linear thermal expansion coefficient have been produced. The findings of this study suggest that solid-electrolytes with negative, positive, or zero linear thermal expansion can be produced to create more compatible and higher-performance solid-state devices.     

Synthesis of a Fe3O4-rGO-ZnO-catalyzed photo-Fenton system with enhanced photocatalytic performance

In this work, we designed a magnetically-separable Fe₃O₄-rGO-ZnO ternary catalyst, ZnO anchored on the surface of reduced graphene oxide (rGO)-wrapped Fe₃O₄ magnetic nanoparticles, where rGO, as an effective interlayer, can enhance the synergistic effect between ZnO and Fe₃O₄. The effects of three operational parameters, namely irradiation time, hydrogen peroxide dosage, and the catalyst dosage, on the photo-Fenton degradation of methylene blue and methyl orange were investigated. The results showed that the Fe₃O₄-rGO-ZnO had great potential for the destruction of organic compounds from wastewater using the Fenton chemical oxidation method at neutral pH. Repeatability of the photocatalytic activity after 5 cycles showed only a tiny drop in the catalytic efficiency.     

New nanocomposite based on poly(lactic-co-glycolic acid) copolymer and magnetite. Synthesis and characterization

The study presents the preparation of the new magnetic nanocomposite based on PLGA and magnetite. The PLGA used to obtain the magnetic nanocomposites was synthesized by the copolymerization of lactic acid with glycolic acid, in the presence of tin octanoate [Sn(Oct)₂] as catalyst, by polycondensation procedure. Magnetite was obtained by co-precipitation from aqueous salt solutions FeCl₂/FeCl₃. The particles size of magnetite was 420 nm, and the saturation magnetization 62.78 emu/g, while the PLGA/magnetite nanocomposite size was 864 nm and the saturation magnetization 39.44 emu/g. The magnetic nanocomposites were characterized by FT-IR, DLS technique, SEM, VSM and simultaneous thermal analyses (TG–FTIR–MS). The polymer matrix PLGA acts as a shell and carrier for the active component, while magnetite is the component which makes targeting possible by external magnetic field manipulation. Based on the gases resulted by thermal degradation of PLGA copolymer, using the simultaneous analysis TG–FTIR–MS, a possible degradation mechanism was proposed.     

Structural,magnetic, thermal and optical properties of Sn2+ cation doped magnetite nanoparticles

Tin doped nanomagnetites, Sn_xFe_3-xO₄, were synthesized with various concentrations of Sn²⁺ ion (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) by co-precipitation method. XRD, VSM, TG-DTA, SEM-EDX and UV–Vis were used to characterize and study the structural, magnetic, thermal, and optical properties of Sn_xFe_3-xO₄ nanoparticles. XRD confirmed the presence of cubic structure and spinel phase of tin doped magnetites. The d-spacing, lattice parameter, density, crystallite size and cation distribution were derived from the XRD analysis. The M − H curves exhibited changes in saturation magnetization (M_s), coercive field (H_c), remanent magnetization (M_r) and susceptibility (χ), with increasing concentration of non-magnetic Sn²⁺ ions. Differential thermal analysis was used to study the thermal stability of Sn_xFe_3-xO₄ nanoparticles. The SEM images revealed the surface morphology of the nanoparticles and the EDX spectra showed an increase in the Sn content and a corresponding decrease in the Fe content for the tin doped samples. The optical bandgap was found to be centered at 3.9 eV for the synthesized materials. This systematic study may be the first comprehensive report on synthesis and characterization of tin doped magnetites.