摘要：为了研究退火温度对镀锌DP980+Z烘烤硬化值的影响，退火温度控制在760～820℃之间，系统分析退火温度对烘烤硬化值的影响。通过准静态拉伸试验机测量烘烤硬化值及抗拉强度，采用lepara试剂对组织中的马氏体进行着色，利用金相显微镜及图像处理软件测量马氏体的体积分数；采用扫描电镜观察DP980+Z的双相组织特点，并且将组织图片通过CAD转化成有限元图进行网格划分，建立代表性体积单元（RVE），通过有限元分析铁素体、马氏体强度对烘烤硬化值的影响。在同样的变形量情况下，DP980+Z的原始屈服强度越高，烘烤硬化值越高。     

微波处理对离体黄瓜子叶生根和根活力的影响

用辐射功率200W微波（2450MHz）处理6～16，明显促进离体黄瓜子叶生根．根长和根鲜重增加。不同辐射强度和辐服时间对离体黄瓜子叶生根有不同影响。用TTC法测定，微波处理后与根活力相关的OD值比对照体增加了。用温箱模拟FISO微波炉功率为200W的温度，不同处理时间处理离体黄瓜子叶，没有发现促进生根。说明在一定条件下，微波辐射处理离体黄瓜子叶促进生根．主要是微波的辐射效应。     

In situ formation of multi scale reinforcing phases to improve performance of Al2O3-SiC C castables

In order to improve the physical properties and slag corrosion resistance of refractory materials for hot metal pretreatment, different contents of composite metal powders (CMP) were introduced into Al2O3-SiC-C refractory castables. The effect of CMP on the microstructure, physical properties and slag corrosion resistance of Al2O3-SiC-C refractory castables were studied. The results show that the multi scale reinforcing phases including flake crystals, rod shaped fibers, filamentous fibers and whiskers are in situ formed in the samples with addition of CMP, which result to the improvement of the cold modulus of rupture and cold crushing strength. When the addition of CMP is 6 wt.%, the high temperature modulus of rupture increases by 231%, the thermal shock resistance increases by 77% after thermal shock by water cooling 5 times and the percentage of the slag resistant area reduces by 37.2%.     

Minimal forbidden subwords

Motivated by a study of similar problems stated for factors of words, we study forbidden subwords of a language or a word. A procedure for obtaining the set of all words avoiding a given set of subwords is presented. On the other hand, an algorithm for computing the set of minimal forbidden subwords for a word is given. The case of a two-letter alphabet appears to be particularly interesting and it is considered separately.     

矩形介质波导阵列的一种新型分析方法

本文将等效介电常数近似分析方法在应用范围和处理方法上进行了一些改进．发展为双等效介电常数近似分析法，然后用它来分析矩形介质波导阵列．推得两个一维周期的耦合特征方程。如果将Macatili方法应用范围扩展用来研究该波导阵列也会得到同样的结果，它们都能在二维平面上较准确地反应出通带和阻带等主要周期特性。     

民族特色词语的英汉互译

语言在其发展演变过程中,逐步具有了鲜明的民族文化色彩。阐述了民族特色词语的可译性,并提出了具体的翻译方法。     

Research and application of automatic control system of argon blowing at ladle shroud

Argon blowing at the ladle shroud requires the best flow control strategy to effectively avoid the secondary oxidation of molten steel, slag entrapment and heat loss during the casting of the tundish, and at the same time, give full play to the role of bubbles to remove inclusions. Therefore, an automatic control system for argon blowing at the ladle shroud was proposed. The data collected by S7-300PLC and software programming were used to adjust the argon blowing flow online in real time according to factors such as pouring and continuous pouring. On this basis, PID control algorithm and closed loop control mechanism were used for real time adjustment. The flow control valve ensures theminimum deviation between the actual value of the flow and the set value. The production data of this system in the first quarter of 2021 in a special steel plant show that the proportion of furnaces with an acid soluble aluminum (Als) loss percentage of less than 10% of each steel grade has increased by 5.52%, and the proportion of furnaces with an Als loss percentage of more than 60% has increased from 1% decrease to 0. The actual application results show that the use of the system improves the surface quality of the continuous casting slab and the performance of the final product.     

水乳型丙烯酸酯建筑防水胶的研制(Ⅱ)

摘 要 研究水乳型丙烯酸酯建筑防水胶与水泥的配比及共混性能、共混固化物胶膜的力学性能、耐冷热性能及老化性能。     

试析当前汉语流行语中的英语借词现象

考察当前汉语流行语中英语借词现象的成因,并分析其不同的吸收方式及各自的理据和语用价值,最后对这一现象今后的发展做出顺应时代且符合语言发展规律的预测.     

Effect of partitioning on microstructure and properties of a medium carbon Ti Mo bearing high strength Q&P steel

In order to investigate the effect of partitioning procedures on microstructure and properties of a medium carbon Ti Mo bearing steel, the salt bath experiment, field emission SEM, TEM and tensile tests as well as wear tests were utilized to clarify the microstructural evolution and property changes treated by different partitioning parameters. The results show that the microstructures consist of tempered lath martensite, cementite and (Ti, Mo)C particles. With prolonging partitioning time or increasing partitioning temperature, the amount of laths martensite decreases and thicker martensite plates with blunt boundaries appear. In addition, with increasing partitioning temperature from 310℃ to 400℃, the tensile strength, hardness and low temperature toughness are simultaneously decreased, and the reduction reaches up to about 300MPa, 100HV and 20J, respectively. Finally, the wear performance of the samples partitioned below Ms is obviously better than that of samples partitioned above Ms. The morphology of worn surface of samples partitioned below Ms is characterized by plastic fatigue morphology, while the worn surfaces of samples partitioned above Ms are mainly dominated by grooves.