无钴黑色陶瓷颜料中铬含量测定的新方法

本文以盐酸羟胺作还原剂,研究了三价铬与二甲酚橙的显色反应,结果发现Cr3 在0～80滋g/50ml范围内,其吸光度与Cr3 含量成正比相关,用于无钴黑色陶瓷颜料中铬含量的测定,作出了回归方程,且进行了显著性检验,获得了理想的结果。     

生物除铬(VI)效果及机理探讨

以特定污泥挂膜的自制厌氧生物滤床系统具有良好的去铬(VI)能力。恒流泵最佳流量为47mL/min,外加碳源使废水COD约140mg/L,铬(VI)的浓度由60mg/L左右降到0.5mg/L以下(一级排放标准),需要4h,而对照组(未加碳源)需要14h。铬(VI)浓度由64.66mg/L提高到75.53mg/L时,对系统负面影响甚微,提高到95.47mg/L时,系统出水达标所需时间延长到7.5h。添加微量金属离子与未添加微量金属离子的情况相比,处理效率提高21.26%。分析试验表明:铬(VI)的去除途径可能是由生物还原作用将六价铬还原为三价铬,形成氢氧化铬沉积于微生物表面。     

Tannins/melamine–urea–formaldehyde (MUF) resins substitution of chrome in leather and its characterization by thermomechanical analysis

A new sulfonated melamine–urea–formaldehyde (MUF) resin of relatively low melamine content, prepared according to a sequential formulation, has been shown to be highly effective when coupled with different natural vegetable tannins to produce leather with the same good characteristics of leather prepared with chrome salts. In particular, the antishrinkage effectiveness of the leather prepared according to the new approach is comparable to that obtained with chrome tanned leathers. The comparison of the traditional leather shrinkage temperatures test method with a new thermomechanical analysis (TMA) test method in tension yields thermograms presenting three major modulus of elasticity (MOE) peaks. These are closely connected to molecular level phenomena determining the shrinkage temperature of leather. The three determining parameters appear to be as follows: (1) The average value of the temperatures at which the three MOE peaks occur: the higher the value of this average, the lower is the shrinkage of leather. (2) The average of maximum MOE values of the TMA peaks: the higher this average is, the better is the leather in regard to antishrinkage effectiveness. This means the leather maximum MOE at each peak is a measure of the resistance to the contraction force induced by heat. (3) The relative intensity of the first TMA peak in relation to the second: the higher the value of the MOE for the first TMA peak is in relation to the second peak, the lower the leather shrinkage appears to be. However, it has not been possible to better define or quantify this latter effect. This new TMA test method in tension has also yielded a mathematical relationship correlating the thermogram peak temperatures and MOE averages with the traditional shrinkage temperature to a high degree of confidence. A previous TMA test method, in compression, has proven to yield more problematic and finally not very reliable results when one needs to apply it to a wide variety of different cases. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 1889–1903, 2003     

多元高铬铸铁在反击式破碎机板锤上的应用

在高铬铸铁中加入多种少量和微量合金元素用以生产反击式破碎机板锤，可使产品耐磨性和综合力学性能得到很大程度的改善。使用寿命比原用高锰钢提高4倍以上。     

烧成温度对高铬砖显微结构的影响

利用扫描电子显微镜分析了 170 0℃、174 0℃、1780℃、182 0℃和 186 0℃烧成后高铬砖的显微结构。结果表明 :高铬砖的烧成温度不是越高越好 ,而是有一个合适的烧成温度 174 0℃。在该烧成温度下制得的高铬砖 ,其基质中的Cr2 O3晶粒尺寸适中 ,基质组织结构致密 ,基质和颗粒结合紧密 ,无裂纹 ,并且其力学性能最佳。     

水煤浆加压气化炉用高铬耐火材料的显微结构及损毁机理

采用扫描电镜和能谱分析方法 ,分析了水煤浆加压气化炉用高铬砖渣蚀前后的显微结构和相组成 ,探讨了主要损毁机理。结果表明 :煤熔渣与砖反应和渗透引起砖组成的改变 ,从而导致砖的结构剥落和强度弱化是砖损毁的主要原因 ;LIRR -HK90砖的显微结构呈网络状镶嵌结构 ,直接结合程度高 ,与渣反应可生成 (Mg ,Fe) (Al,Cr,Fe) 2 O4 复合尖晶石致密带 ,阻止了渣的进一步渗透 ,减缓渣蚀速度和结构剥落 ,其使用效果优于进口的同类产品     

治理铬渣的两个关键

铬渣中存在的酸溶性六价铬是解毒效果能否持久的关键，而铬渣中游离氧化镁消化是利用铬渣作建筑材料时必须高度重视的问题，论述了湿法解毒、高温解毒和非熔融的综合利用法等方法，对铬盐行业的铬渣治理有指导作用。     

30CrMnSiNi2A钢件镀硬铬的氢脆分析

本文叙述了用延迟破坏法试验超高强度钢(υb=1700MPa)不超过三次镀硬铬的氢脆情况。     

浸渍铁铬对灵石焦煤在热解过程中逸出气体的影响

利用GC-FPD和TPD-MS考察了浸渍Fe3+和Cr3+对灵石煤热解过程中气体产物逸出的影响.结果表明:Fe3+和Cr3+破坏了煤中的氢键并与煤表面官能团形成活性络合物,使煤样的挥发分增加、固定碳等减少;由于Fe3+的氧化作用,载铁煤中的黄铁矿硫明显减少.低于300℃时,Fe3+和Cr3+促进煤中有机硫分解,增加了H2S和SO2的生成量;300～700℃时,由于Fe3+和Cr3+的固硫反应,转移到气相中的硫急剧减少;700℃时置换为氮气和氢气混合气后,在高温还原性气氛下,Fe和Cr的固硫产物和稳定的有机硫加氢脱硫产生大量的H2S.由于Fe3+和Cr3+促进了煤的热解和初级焦油裂解,CO2,CO,H2O,CH4的生成量增加;金属离子对芳香结构缩聚反应的促进作用增加了H2的生成量,Cr3+对灵石焦煤热解过程中逸出气体的影响强于Fe3+.     

镀铬对光刻胶全息光栅掩模槽形的影响

为了研究镀铬对光刻胶光栅掩模槽形的影响,分析了铬膜反射引起的沿垂直光刻胶表面的驻波效应。分析表明驻波效应的对比度为0.28,不能忽略。将镀铬基底与普通的玻璃基底的掩模槽形对比,发现明显的不同。槽形模拟表明这种不同是由于驻波效应引起的。驻波效应会使掩模形成阶梯结构,且阶梯高度差正好为驻波波节间距离。