Effect of select parameters on the properties of edible film from water-soluble fish proteins in surimi wash-water

Edible film from water-soluble fish proteins were developed by casting film solution on leveled trays and effects of pH (9.5, 10.0 and 10.5), heating temperature (60, 70 and 80 °C), and heating time (10, 20 and 30 min) of the film solution on various film properties were determined using Response Surface Methodology (RSM). The impact of pH and heating temperature of film solution was more significant, overall, on the film's properties than heating time. Contour plots of tensile strength and elongation at break was highest at pH of 10.0 at 70 °C (2.75-3.02 MPa) but low in elongation at break (6.35-9.16%), while water vapor permeability and oxygen permeability were at their lowest (58.55-65.96 g mm/m² d kPa and 351.33-624.18 cm³ μm/m² d kPa). There was a direct correlation between the films’ and proteins’ solubility on one hand, and heating temperature of film solution on the other, which reversed with change in pH of film solution. Film color was darker and more yellowish with increase in the pH of film solution.     

新型高K栅介质ZrO2薄膜材料的制备及表征

采用超高真空电子束蒸发法制备了新型高 K栅介质-非晶 ZrO2薄膜. X射线光电子能谱 (XPS) 中 Zr3d5/2 和 Zr3d3/2 对应的结合能分别为 182.1eV和 184.3eV, Zr元素的主要存在形式为 Zr4+,说明薄膜由完全氧化的 ZrO2组成 ,并且纵向分布均一.扩展电阻法( SRP)显示 ZrO2薄膜的 电阻率在 108Ω@ cm以上,通过高分辨率透射电镜( HR- XTEM)可以观察 ZrO2/Si界面陡直,没有 界面反应产物 ,证明 600℃快速退火后 ZrO2薄膜是非晶结构.原子力显微镜( AFM)表征了薄膜的 表面粗糙度,所有样品表面都很平整,其中 600℃快速退火样品 (RTA)的 RMS为 0.480nm.     

Influence of Polyalkylmethacrylate VII on Boundary Film Formation,Friction,Wear and Efficiency of Lubricants

1 Influence of PAMAon Boundary Fil mFormation and Friction1.1 Experi mental methodsUltra-thin optical interferometry has been used tostudy thinlubricating fil ms for more than a decade and theexperi mental details of this technique have been reportedpreviously[1].The principle of the test setup is shown inFigure1.A polished steel ball is loaded and rolled againstthe flat surface of a glass disc that is coated with a thinsemi-reflecting chromiumlayer and a silica spacer of about500nmthickne…     

Nonstationary Simulation Model of Absorber with Falling Film of Suspension

A nonstationary model of SO₂ absorption from a gas phase to a countercurrent falling film of absorbing slurry was developed. Laminar, wavy and turbulent film structures were considered based on published information. Resistances to the mass transfer on the gas and the liquid sides of the interphase were considered, together with chemical reactions in the liquid phase. Relevant chemical equilibria in the liquid phase were modeled. Original experimental data on the neutralization reagent dissolution rate presented as a polydispersed two‐phase system of solids and on the rate of dissolved sulfite oxidation were used. The model was verified with experimental data from a laboratory‐scale falling‐film absorber using a single vertical tube under various geometrical and operating conditions, and a very good agreement was found with the experiment. Parametric sensitivity analysis showed the critical parts of the model.     

Gamma-irradiation-induced Ag/SiO2 composite films and their optical absorption properties

Small Ag particles or clusters dispersed mesoporous SiO₂ composite films were prepared by a new method: First the matrix SiO₂ films were prepared by sol-gel process combined with the dip-coating technique, then they were soaked in AgNO₃ solutions followed by irradiation of γ-ray at room temperature and in ambient pressure. The structures of these films were examined by X-ray diffraction (XRD), high-resolution transmission electron microscope (HRTEM), and optical absorption spectroscopy. It has been shown that the Ag particles grown within the porous SiO₂ films are very small, and they are isolated and dispersed from each other with very narrow size distributions. With increasing the soaking concentration and an additional annealing, an opposite peakshift effect of the surface plasmon resonance (SPR) was observed in the optical absorption measurements.     

L－B膜修饰电极循环伏安行为模拟──（Ⅰ）电荷转移速度常数对循环伏安性能的影响

本文用计算机数字模拟方法研究了电活性分子多层Ｚ型Ｌ－Ｂ膜修饰电极的循环伏安行为。计算了电极与修饰Ｌ－Ｂ膜分子第一层之间的电荷转移速度常数Ｋ_ｏ，Ｌ－Ｂ膜分子层间的电荷转移速度常数ｋ_ｉ；对峰电位差△Ｅ_ｐ及阳极峰面积Ｑ的影响，以及在不同条件下各层分子的氧化态分数随扫描时间的变化。为研究和设计电活性分子修饰电极的实际体系提供了大量数据和信息。     

预处理工艺对硬质合金与金刚石膜间粘结力的影响

在两种经不同预处理的硬质合金YG8基底上，采用微波等离子体化学气相沉积法，在微波功率2kW，压强4.0kPa和6.5kPa，CH4和H2流量分别为1.6cm/s和100.0cm/s的条件下生长金刚石薄膜。利用X射线衍射检测了金刚石薄膜是否存在，用拉曼光谱分析了薄膜的质量，用金相显微镜观察了薄膜的洛氏硬度压痕，标定并比较了不同预处理工艺膜与基底的结合力。实验结果表明，不同的预处理方法对于粘结力的影响不大，最主要的因素是钴含量的多少。     

The microstructure of Cu films deposited by the self-ion assisted technique

The microstructures of Cu films deposited by the self-ion assisted, partially ionized beam (PIB) deposition technique under two different accelerating potentials, 0 KeV and 6 KeV, are compared. The 6 KeV film shows a bimodal (111) fiber and (100) fiber texture with an abundance of twin boundaries and a relatively large average grain size with a typical lognormal distribution. The 0 KeV film consists of small, mostly (111) oriented grains with islands of abnormally large (100) grains. The controlling factors for the abnormal growth of the (100) grains are discussed in relation to the observed microstructures, showing that all factors necessary for abnormal (100) growth are present in the films.     

金刚石膜的计算机虚拟制备技术中的分子动力学模拟

综述了近年来金刚石薄膜形成过程的分子动力学（Molecular Dynamics，简称MD）模拟研究，详细地阐述了原子间相互作用势的选取，总结了不同沉积条件下MD的计算模型和几种典型情况下的模拟结果。研究表明：在原子尺度上，MD方法能较全面地提供有关膜生长的信息，对进一步了解金刚石膜形成的微观机制以及为细观层次仿真提供基本信息均具有重要意义。