Ablation resistance of SiC‐modified ZrC coating prepared by SAPS for SiC‐coated carbon/carbon composites

This study evaluated the ablation resistance of ZrC/SiC coating for carbon/carbon (C/C) composites at different temperatures and heat fluxes, which improved the researches on ultra‐high temperature oxidation of ZrC/SiC system. Results showed that the protection of coating depended on temperature and heat flux. Ablation test for 120 seconds under heat flux of 2.4 MW/m² at 2270°C revealed a good ablation resistance, with the linear ablation rate reduced by 96.4% and the mass gain rate increased by 383.3% compared with those of pure ZrC coating. The good ablation resistance was attributed to the formation of dense oxide scale surface. SiC could improve the compactness of the oxide scale at this temperature by forming SiO₂. A dense scale could not form at 2105°C after ablation for 120 seconds, resulting in a dissatisfactory ablation resistance of the coating. After ablation for 120 seconds at 1738°C, the coating was integrated due to the protection of glassy SiO₂ encapsulated ZrO₂. The coating could not resist the strong shear force from the flame at heat flux of 4.2 MW/m² and was severely damaged after ablation for 60 seconds.