| 原位聚合增密次数对C/C复合材料性能的影响 |
| |
| 引用本文： | 孙超,张博,杨晓光,许正辉,宋怀河,花双平,陈晓红.原位聚合增密次数对C/C复合材料性能的影响[J].新型炭材料,2012,27(1):49-54. |
| |
| 作者姓名： | 孙超 张博 杨晓光 许正辉 宋怀河 花双平 陈晓红 |
| |
| 作者单位： | 1. 北京化工大学化工资源有效利用国家重点实验室,北京,100029
2. 航天材料及工艺研究所先进功能复合材料技术国防科技重点实验室,北京,100076 |
| |
| 摘 要： | 以萘为基体碳源,Lewis酸为催化剂,通过对芳烃小分子的催化缩聚建立了一种新型原位聚合C/C复合材料的增密方法。分别对两种不同密度的炭纤维增强C/C复合材料预制体进行致密化处理,研究了原位增密次数对材料体积密度、电阻率、弯曲强度和断面形貌的影响。结果表明:经过五次致密化循环,样品密度分别由原来的1.05 g/cm3和1.68g/cm3提高到1.52g/cm3和1.83g/cm3,电阻率由4.44mΩ.cm和0.84mΩ.cm降至1.09mΩ.cm和0.28mΩ.cm,弯曲强度由26MPa和86MPa增至95MPa和211MPa,说明原位聚合增密方法非常有利于快速提高复合材料的密度和其他物理性能,是一种有前途的增密新途径。
|
| 关 键 词： | 原位聚合 致密化 体积密度 电阻率 弯曲强度 |
Effect of cycle time of in-situ polymerization of naphthalene on the densification and performance of C/C composites |
| |
| SUN Chao
,
ZHANG Bo
,
YANG Xiao-guang
,
XU Zheng-hui
,
SONG Huai-he
,
HUA Shuang-ping
,
CHEN Xiao-hong.Effect of cycle time of in-situ polymerization of naphthalene on the densification and performance of C/C composites[J].New Carbon Materials,2012,27(1):49-54. |
| |
| Authors: | SUN Chao ZHANG Bo YANG Xiao-guang XU Zheng-hui SONG Huai-he HUA Shuang-ping CHEN Xiao-hong |
| |
| Affiliation: | 1(1.State Key Laboratory of Chemical Resource Engineering,Beijing University of Chemical Technology,Beijing 100029,China; 2.National Key Laboratory of Advanced Functional Composite Materials,Aerospace Research Institute of Materials and Processing Technology, Beijing 100076,China) |
| |
| Abstract: | A rapid densification approach for the fabrication of C/C composites was developed by in-situ polymerization of naphthalene with a Lewis acid as catalyst in two preforms of 3D braided carbon fiber/pyrocarbon composites with different densities.The effects of cycle time on the fracture morphology,bulk density,electrical resistivity and flexural strength of the C/C composites were investigated.Results showed that the bulk densities of the C/C preforms increased from 1.05 to 1.52 g/cm3and from 1.68 to 1.83 g/cm3,their electrical resistivity decreased from 4.44 to 1.09 mΩ · cm and 0.84 to 0.28 mΩ · cm,and their flexural strength increased from 26 to 95 MPa and 86 to 211 MPa respectively after five cycles.In-situ polymerization is a simple,effective,competitive and rapid densification approach for the fabrication of C/C composites. |
| |
| Keywords: | In-Situ Polymerization Densification Bulk Density Electrical Resistivity Flexural Strength |