Optical Properties of Dysprosium-Doped Low-Phonon-Energy Glasses for a Potential 1.3 μm Optical Amplifier

Dysprosium-doped glasses were prepared in the system of gallium-based sulfide, tellurite, zirconium-baed and indium-based fluorides and their optical properties were studied. From the absorption cross sections of five f-f bands, three Judd-Ofelt parameters, ω _t ( t = 2, 4, 6), of Dy³⁺ ion were determined. The compositional variaton of the ω₂value showed the order sulfide > tellurite > fluorozirconate > fluoroindate, whereas the ω₆ value showed the opposite tendency. Compositional variaton of the fluorescence intensity ratio of the (⁴F_9/2⁶H_13/2)/(⁴F_9/2)→⁶H_15/2) is explained by the ratio of ω₂/ω₆ of doped Dy³⁺. The emission probabilities A and the branching ratio β from ⁶H_9/2 and ⁶F_11/2 levels, which are the doublet initial level of the 1.3 μm luminescence, were calculated for the glasses, and it was found that both values showed a tendency similar to that of ω₂ against the glass composition. In the sulfide glass, A was 2.6 × 10³S^-1 and β was 93%, both the highest in all of the glasses investigated. By 1.06 μm pumping of a Nd: YAG laser, the sulfide glass showed strong 1.3 μm emission and the lifetime was 25 μs, resulting in a quantum efficiency of 7%. This value is higher than that of the Pr³⁺:¹G₄ level in ZBLAN glass with β= 60%.