Phonon scattering and thermal conduction mechanisms of sintered aluminium nitride ceramics |
| |
Authors: | Koji Watari Kozo Ishizaki Fumiaki Tsuchiya |
| |
Affiliation: | (1) Ceramics Science Department, Government Industrial Research Institute Nagoya, Hirate-cho, Kita-ku, 462 Nagoya, Japan;(2) Department of Materials Science and Engineering, School of Mechanical Engineering, Nagaoka University of Technology, Nagaoka, 940-21 Niigata, Japan;(3) Mitsubishi Heavy Industries, Oye-cho, Minato-ku, 455 Nagoya, Japan |
| |
Abstract: | From thermal diffusivity measurements of sintered AIN at temperatures ranging from 100 to 1000 K, the phonon mean free path of AIN was calculated in order to investigate phonon scattering mechanisms. The calculated mean phonon scattering distance was increased with decreasing temperature. The mean phonon-defect scattering distances were respectively limited to about 50 nm at temperatures ranging from 100 to 270 K and about 30 nm at temperatures ranging from 100 to 700 K, for AIN specimens with a room-temperature thermal conductivity of 220 and 121 Wm–1 K–1 containing 0.1 and 1.4 wt % oxygen, respectively. These short phonon-defect scattering distances were considered to correspond to the separation of oxygen-related internal defects in AIN grains. Calculation of the mean phonon scattering frequencies indicated that the phonon scattering is dominated by phonon-defect scattering at temperatures below 270 K for an AIN specimen with an oxygen content of 0.1 wt %, and at temperatures below 350 K for an AIN specimen with an oxygen content of 1.4 wt %. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|