Spectral analysis of RE (RE = Sm, Dy, and Tm): P2O5–Al2O3–Na2O glasses

Phosphate glasses in the compositions of 70P₂O₅–15Al₂O₃–14Na₂O–1RE³⁺ (RE = Sm, Dy, and Tm) (mol%) were prepared by melt-quenching technique and characterized optically. The differential thermal analysis (DTA) profile of the host glass was carried out to confirm its thermal stability. For all the glasses absorption, photoluminescence and decay measurements have also been carried out. These glasses have shown strong emission and absorption bands in visible and near-infrared (NIR) region. From the measured absorption spectra, Judd–Ofelt (J–O) intensity parameters (Ω₂, Ω₄ and Ω₆) have been calculated for all the studied ions. For Sm³⁺ doped glass, four emission bands centered at 562 nm (⁴G_5/2 → ⁶H_5/2), 598 nm (⁴G_5/2 → ⁶H_7/2), 644 nm (⁴G_5/2 → ⁶H_9/2), and 704 nm (⁴G_5/2 → ⁶H_11/2) have been observed with 402 nm (⁶H_5/2 → ⁴F_7/2) excitation wavelength. Of them, 598 nm (⁴G_5/2 → ⁶H_7/2) has shown a bright orange emission. With regard to Dy³⁺ doped glass, a blue emission band centered at 486 nm (⁴F_9/2 → ⁶H_15/2) and a bright yellow emission at 575 nm (⁴F_9/2 → ⁶H_13/2) have been observed, apart from 662 nm (⁴F_9/2 → ⁶H_11/2) emission transition with an excitation at 388 nm (⁶H_15/2 → ⁴I_13/2,⁴F_7/2) wavelength. Emission bands of 650 nm (¹G₄ → ³F₄) and 785 nm (¹G₄ → ³H₅) transitions for the Tm³⁺ doped glass, with an excitation wavelength at 466 nm (³H₆ → ¹G₄), have also been observed. The stimulated emission cross-sections of all the emission bands of RE³⁺ glasses (RE = Sm, Dy, and Tm) have been computed based on their measured full-width at half maximum (FWHM, Δλ) and measured lifetimes (τ_m).