Growth temperature dependent dielectric properties of BiFeO3 thin films deposited on silica glass substrates

We have studied the dependence of dielectric properties on the deposition temperature of BiFeO₃ thin films grown by the pulsed laser deposition technique. Thin films have been grown onto amorphous silica glass substrates with pre-patterned Au in-plane capacitor structures. It is shown that on the amorphous glass substrate, BiFeO₃ films with a near-bulk permittivity of 26 and coercive field of 80 kV/cm may be grown at a deposition temperature of about 600 °C and 1 Pa oxygen pressure. Low permittivity and higher coercive field of the films grown at the temperatures below and above 600 °C are associated with an increased amount of secondary phases. It is also shown that the deposition of BiFeO₃ at low temperature (i.e. 500 °C) and post deposition ex-situ annealing at elevated temperature (700 °C) increases the permittivity of a film. The applied bias and time dependence of capacitance of the films deposited at 700 °C and ex-situ annealed films are explained by the de-pinning of the ferroelectric domain-walls.