| Abstract: | The curing kinetics of dimethacrylate-based vinyl ester resins were studied by scanning and isothermal DSC, gel time studies, and by DMTA. The rate of polymerization was raised by increased methyl ethyl ketone peroxide (MEKP) concentration but the cocatalyst, cobalt octoate, retarded the reaction rate, except at very low concentrations. By contrast, the gel time was reduced for all increases in either peroxide or cobalt concentration. This contradictory behavior was explained by a kinetic scheme in which the cobalt species play a dual role of catalyzing the formation of radicals from MEKP and of destroying the primary and polymeric radicals. The scanning DSC curves exhibited multiple peaks as observed by other workers, but in the present work, these peaks were attributed to the individual influence of temperature on each of fundamental reaction steps in the free radical polymerization. Physical aging appeared to occur during the isothermal polymerization of samples cured below the “fully cured” glass transition temperature (Tg). For these undercured materials, the difference between the DSC Tg and the isothermal curing temperature was approximately 11°C. Dynamic mechanical analysis of a partially cured sample exhibited anomalous behavior caused by the reinitiation of cure of the sample during the DMTA experiment. For partially cured resins, the DSC Tg increased monotonically with the degree of cure, and this dependence was fitted to an equation related to the Couchman and DiBenedetto equations. © 1997 John Wiley & Sons, Inc. J Appl Polym Sci 64: 769–781, 1997 |