Deposition of Sm2O3 doped CeO2 thin films from Ce(DPM)4 and Sm(DPM)3 (DPM=2,2,6,6-tetramethyl-3,5-heptanedionato) by aerosol-assisted metal–organic chemical vapor deposition

Samarium-doped ceria (SDC) thin films were prepared from Sm(DPM)₃ (DPM = 2,2,6,6-tetramethyl-3,5-heptanedionato) and Ce(DPM)₄ using the aerosol-assisted metal–organic chemical vapor deposition method. -Al₂O₃ and NiO-YSZ (YSZ = Y₂O₃-stabilized ZrO₂) disks were chosen as substrates in order to investigate the difference in the growth process on the two substrates. Single cubic structure could be obtained on either -Al₂O₃ or NiO-YSZ substrates at deposition temperatures above 450 °C; the similar structure between YSZ and SDC results in matching growth compared with the deposition on -Al₂O₃ substrate. A typical columnar structure could be obtained at 650 °C on -Al₂O₃ substrate and a more uniform surface was produced on NiO-YSZ substrate at 500 °C. The composition of SDC film deposited at 450 °C is close to that of precursor solution (Sm : Ce = 1 : 4), higher or lower deposition temperature will both lead to sharp deviation from this elemental ratio. The different thermal properties of Sm(DPM)₃ and Ce(DPM)₄ may be the key reason for the variation in composition with the increase of deposition temperature.