Interfacial microstructure and properties of Sn-0.7Cu-0.05Ni/Cu solder joint with rare earth Nd addition |
| |
| Authors: | Guang ZengSongbai Xue Lili GaoLiang Zhang Yuhua HuZhongmin Lai |
| |
| Affiliation: | a College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, No. 29 Yudao Street, Nanjing 210016, Jiangsu Province, People''s Republic of China
b Provincial Key Lab of Advanced Welding Technology, Jiangsu University of Science and Technology, Zhenjiang 212003, People''s Republic of China |
| |
| Abstract: | Interfacial microstructure and properties of Sn-0.7Cu-0.05Ni/Cu solder joints with trace amounts Nd additions have been investigated in this paper. The evolution of interfacial morphology of SCN solder joints with and without the presence of Nd under long-term room ambience was also studied. The greatest improvement to the solderability and tensile strength of SCN-xNd are obtained at 0.05 wt.% Nd. Meanwhile, the morphology and growth of interfacial intermetallic (IMC) layer are greatly improved by adding Nd, and the propensity for IMC spalling from the interface of solder joint is definitely reduced with the presence of rare earth Nd, since the sponge-like structure was completely inhibited in the solder joint containing Nd. In addition, a significant amount of Sn whiskers were present on the surface of NdSn3 phases in the SCN0.15Nd/Cu solder joints, and the reason for this phenomenon has been briefly discussed. |
| |
| Keywords: | Metals Mechanical property Microstructure |
| 本文献已被 ScienceDirect 等数据库收录！ |
|