Preparation of ultrafine polyurethane fiber web by laser‐electrospinning combined with air blowing
Authors:Midori Takasaki  Kentaro Hara  Yutaka Ohkoshi  Takayuki Fujii  Hiroyasu Shimizu  Masaharu Saito
Affiliation:1. Division of Domestic Science Education, Faculty of Education, Miyagi University of Education, , Sendai, 980‐0845 Japan;2. Department of Advanced Textile Engineering, Faculty of Textile Science and Technology, Shinshu University, , Nagano, 386‐8567 Japan;3. KB SEIREN LTD, , Fukui, 916‐0038 Japan
Abstract:Thermoplastic polyurethane fiber webs were prepared using a laser‐heated electrospinning process combined with air blowing. The effect of spinning conditions such as air flow rate and air temperature on fiber diameter and molecular weight was investigated. Although the average fiber diameter decreased with increased air flow rate at each air temperature, the diameter increased when the air flow rate was >15 NL min?1. In addition, the fiber was comparatively thicker with an increase in the air temperature. The variation in the fiber diameter tends to increase with the air flow rate, and a reduction in the molecular weight of the fiber by thermal degradation was suppressed. The thinnest and most uniform fiber with a diameter of 0.9 µm and a diameter coefficient variation of 15% was obtained at an air temperature of 25°C under an air flow rate of 15 NL min?1. This fiber also had a minimum of decreased molecular weight. POLYM. ENG. SCI., 54:2605–2609, 2014. © 2013 Society of Plastics Engineers
Keywords:
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号