Low temperature preparation of the Zn2SiO4 ceramics with the addition of BaO and B2O3

The Zn₂SiO₄ ceramics with the addition of BaO and B₂O₃ are fabricated by traditional solid-state preparation process at a sintering temperature of 900 °C. The introduction of BaO and B₂O₃ to the binary system ZnO-SiO₂ is achieved by adding 10 and 20 wt. % flux BB to the mixed ZnO-SiO₂ ceramic powders pre-sintered at 1,100 °C, respectively. The chemical composition of the flux BB (50 wt.%BaO-50 wt.% B₂O₃) is located at a liquid phase zone with a temperature range of about 869–900 °C in the binary diagram BaO-B₂O₃. In addition, the introduction of BaO and B₂O₃ to the binary system ZnO-SiO₂ is also achieved by the means of a chemical combination of H₂SiO₃, H₃BO₃, ZnO and Ba(OH)₂·8H₂O, which can result in the formation of the hydrated barium borates with low melting characteristics. In turn, by the liquid sintering aid of the barium borate melts, the preparation process of the Zn₂SiO₄ ceramics can be further simplified. In the two preparation methods, the Zn₂SiO₄ ceramics with the 1.5–2.0 ZnO/SiO₂ molar ratios and the addition of a 10 wt. % flux BB can show good dielectric properties whereas the bending strength mainly depends on the microstructure of the Zn₂SiO₄ ceramics and SiO₂ content in the composition of the specimen.