Microwave dielectric properties of rutile (Zn1/3Nb2/3)0.40(Ti1−xSnx)0.60O2 (0.15 ≤ x ≤ 0.30) ceramics

Microwave dielectric properties of (Zn_1/3Nb_2/3)_0.40(Ti_1?xSn_x)_0.60O₂ ceramics were investigated as a function of SnO₂ content (0.15 ≤ x ≤ 0.30). A single phase with tetragonal rutile structure was obtained through the entire composition. The unit-cell volume of the specimens was increased with SnO₂ content, due to the larger ionic radius of Sn⁴⁺ (0.69 Å) than that of Ti⁴⁺ (0.605 Å) for octahedral site. Dielectric constant (K) of the sintered specimens was affected by the dielectric polarizability. Quality factor (Qf) was dependent on the degree of reduction of Ti⁴⁺ ion. With an increase of SnO₂ content, the temperature coefficient of resonant frequency (TCF) of the specimens decreased due to the decrease of the octahedral distortion of rutile structure.