| Abstract: | ABSTRACT The flexural behavior of ferrite filled poly-ether-ether-ketone (PEEK) composites, with and without reinforcement of nano-barium titanate, was studied and was corroborated through scanning electron microscopy (SEM). In this study, ferrite filled PEEK, and ferrite and nano-barium titanate reinforced PEEK composites were prepared. Ferrite filled PEEK composites showed reduction in flexural strength and increase in flexural modulus with the increase in ferrite content, whereas, with the reinforcement of nano-barium titanate, flexural strength increased and flexural modulus decreased at similar ferrite content. The SEM micrographs corroborated well with flexural behavior, as ferrite particles and smooth topographic surfaces of brittle fracture were evident in the samples having higher ferrite content in ferrite filled PEEK composites, whereas, typical yield pattern of crust and trough on fractured topographic surfaces of ferrite and nano-barium titanate, reinforced PEEK composites, was visible. |