| Abstract: | Four kinds of compatibilizers—chlorinated polyethylene (normal CPE), highly chlorinated CPE, maleic anhydride grafted with polypropylene (MP), and chlorinated polypropylene (CPP)—were used to study the influence of compatibilizing agents on the properties of nitrile-butadiene rubber and polypropylene (NBR/PP) blends, a kind of thermoplastic elastomer (TPE). The results show that the most proper amount of normal CPE, highly chlorinated CPE, MP, and CPP are 9, 8, 7, and 6 wt%, respectively, in the NBR/PP blends. The CPP was the best compatibilizer for NBR/PP blends among the four. NBR/PP blends obtained excellent properties of thermoplastic materials and can be molded with the general processing technologies for thermoplastics, such as injection, extrusion, blow molding, and the like. The mechanical properties are similar to that of Geolast, produced by Monsanto Company, and exceed the Chinese national criterion (GB7527-87). The tensile strength was 13.8 MPa; the elongation at break was 290%; and the compression set was 32%. After the blends were immersed in oil for 70 h, the tensile strength was 10.4 MPa, and the degree of oil absorption was 12%. The compatibility of the blends was consistent with the morphology from transmission electron microscopy (TEM). |