Long multifilament Bi-2223 Ag-sheathed superconducting tapes and solenoids

Multifilament Ag-sheathed BiPbSrCaCuO (2223) superconducting tapes containing 49 filaments were fabricated by the powder-in-tube route and the roll-anneal process. The transport critical current densityJ_c was 1.3×10⁴ A cm^–2 at 77 K and 7×10⁴ A cm^–2 at 4.2 K in self-field. A 12-m-long tape was used to construct superconducting solenoids (50, 28, and 14 mm internal diameters) generating dc fields 380–1070 G at 4.2 K. Measurements of the variation ofJ_c with field (0–1.6 T) and bend strain (0–5%) are used to explain the performance of the solenoids. The critical bend strain of tapes was about 1.5%.