Tribological Properties of a Dendrite-reinforced Ti-based Metallic Glass Matrix Composite under Different Conditions |
| |
Affiliation: | Research Institute of Surface Engineering,Taiyuan University of Technology,Taiyuan 030024,Shanxi,China |
| |
Abstract: | The tribological properties of the in-situ dendrite-reinforced metallic glass matrix composite (Ti42 Zr22 V1 4-Cu5 Be1 7 )prepared by copper mould casting were analyzed at different normal loads under the dry condition and rain-water.The results showed that the average value of the frictional coefficients and micro-hardness ascended with in-creasing the normal load,while the wear rate showed a trend of decline under the dry condition.The electrochemical test results showed that the surface of samples was pitting corroded in the rainwater.The matrices were corroded first.Then the dendrites were exposed,leading to the damage of the surface.Both the frictional coefficients and wear rate of the composite in the rainwater were larger than those under the dry condition,primarily owing to the corro-sion of chloride ions on the worn surface.The wear mechanisms of composites were mainly adhesive wear,accompa-nied by the abrasive wear under the dry condition and corrosive wear in the rainwater.The composites have higher wear resistance both under the dry condition and rainwater due to the lower wear rate. |
| |
Keywords: | sliding wear surface topography electrochemical test pitting corrosion |
本文献已被 CNKI 万方数据 等数据库收录! |
|