| 022Cr25Ni7Mo4N的热穿孔和冷加工工艺 |
| |
| 引用本文： | 沈国雄,徐见平,吴汉民,夏亚金,张云恒,张建国.022Cr25Ni7Mo4N的热穿孔和冷加工工艺[J].钢铁研究学报,2016,28(5):70-74. |
| |
| 作者姓名： | 沈国雄 徐见平 吴汉民 夏亚金 张云恒 张建国 |
| |
| 作者单位： | 浙江中达特钢股份有限公司,浙江海盐,314312 |
| |
| 摘 要： | 通过在AOD冶炼的热轧(直径65 mm)圆管022Cr25Ni7Mo4N钢坯上切取试样,研究不同的热穿孔和冷加工工艺参数对钢中两相(铁素体和奥氏体)的比例、σ相析出和溶解特点及对钢性能的影响.结果表明:σ相析出的敏感温度区为850～900℃,σ相完全溶解温度为1 010℃.结合热穿孔的特点,圆管坯热穿孔的加热温度为1080～1180℃.为避免加热过程中产生裂纹的可能,在σ相析出的温度区内,应避免重复加热或长时间保温.采用合适的热穿孔和冷加工工艺后,无缝钢管成品满足相关标准的要求.
|
| 关 键 词： | 超级双相不锈钢022Cr25Ni7Mo4N 热穿孔 σ相 中间退火处理 成品固溶处理 |
Processes of hot piercing and cold working for 022Cr25Ni7Mo4N |
| |
| SHEN Guo- xiong,XU Jian- ping,WU Han- min,XIA Ya- jin,ZHANG Yun- heng,ZHANG Jian- guo.Processes of hot piercing and cold working for 022Cr25Ni7Mo4N[J].Journal of Iron and Steel Research,2016,28(5):70-74. |
| |
| Authors: | SHEN Guo- xiong XU Jian- ping WU Han- min XIA Ya- jin ZHANG Yun- heng ZHANG Jian- guo |
| |
| Affiliation: | ??Zhejiang Zhongda Special Steel Co., Ltd., Haiyan 314312?? Zhejiang?? China?? |
| |
| Abstract: | Samples were taken from φ65 mm round tube blank of 022Cr25Ni7Mo4N after AOD and hot rolling.Tests were made with different parameters of hot piercing and cold working to find relationship among them and the ratio of two phases,characteristics of precipitation and dissolution of σ phase and the properties.The results show that σ phase precipitates at 850-900 ℃.Complete dissolution temperature of σ phase is 1 010 ℃.Combining with characteristics of hot piercing,the heating temperature should be 1080-1180 ℃.Repeated heating and long time heating in precipitate temperature range of σ phase should be avoided to eliminate crack during heating.With suitable parameters of hot piercing and cold working,seamless tubes can meet requirements of relevant standards. |
| |
| Keywords: | super duplex phase stainless steel 022Cr25Ni7Mo4N hot piercing σ phase inter-pass annealing treatment final solution treatment |