Extrusion of PE/PS blends with supercritical carbon dioxide

The effects of dissolved supercritical carbon dioxide on the viscosity and morphological properties were investigated for polyethylene/polystyrene blends in a twin-screw extruder. The viscosities of the blend/CO₂ solutions were measured using a wedge die mounted on the extruder. A considerable reduction of viscosity was found when CO₂ was dissolved in the blend. It was observed that the dissolution of CO₂ into PE/PS blends, regardless of the CO₂ content used, led to decreased shear thinning behavior resulting in an increase of the power law index from 0.29 to 0.34. The cell structures of foamed PE/PS blends showed a typical dependence of pressure and CO₂ concentration, with higher operating pressures and CO₂ content leading to a smaller cell size. Also, it was noted that the size of the dispersed PS phase in the PE/PS phase blends decreased by increasing the CO₂ concentration, and that the dispersed PS phase domains were highly elongated in the direction normal to the cell radius.