Effect of electrolyte on electrochemical characteristics of MmNi3.55Co0.72Al0.3Mn0.43 alloy electrode for hydrogen storage

A series of experiments have been performed to investigate the effects of three electrolytes of different compositions (EO, EA and EM) on the electrochemical characteristics of MmNi_3.55Co_0.72Al_0.3Mn_0.43 hydrogen storage alloy electrode. Electrolytes EA and EM were obtained by adding appropriate amounts of Al₂(SO₄)₃ and MnSO₄ to the original electrolyte EO (6 M KOH + 1 wt% LiOH), respectively. Electrode activation, maximum capacity, cycle life, self-discharge and high-rate discharge characteristics have been studied. It was found that a maximum capacity of about 260 mA h/g has been obtained for the alloy electrodes in all these electrolytes after 5–7 cycles of charging/discharging. The alloy electrodes have a good durability in electrolytes EA and EM, especially after 175 cycles. Using the capacity retention as an indication of self-discharge resistance, almost identical degree of capacity retention (82% after 4 days and 45% after 16 days) has been observed at 298 K, regardless of the electrolytes used. When tested at higher temperature, however, a higher capacity retention (46% after 3 days) at 333 K has been observed for electrodes in electrolyte EA, and about 32% for electrodes in both electrolytes EO and EM. As to high-rate discharge behavior of the results of high-rate discharge tests indicated that about 50% of discharge efficiencies were obtained in the three electrolytes at 333 K by continuous-model high-rate discharge method, at a discharge rate of 7C, and 22% in 298 K. The alloy electrode in electrolyte EM has the best durability, in which about 50% of discharge efficiency at DC = 9C was obtained by step-model high-rate discharge method at 333 K, which was even higher than that at 298 K.