Stabilized zirconia-based sensor utilizing SnO2-based sensing electrode with an integrated Cr2O3 catalyst layer for sensitive and selective detection of hydrogen

A highly selective hydrogen (H₂) sensor has been successfully developed by using an yttria-stabilized zirconia (YSZ)-based mixed-potential-type sensor utilizing SnO₂ (+30 wt.% YSZ) sensing electrode (SE) with an intermediate Al₂O₃ barrier layer which was coated with a catalyst layer of Cr₂O₃. The sensor utilizing SnO₂ (+30 wt.% YSZ)-SE was found to be capable of detecting H₂ and propene (C₃H₆) sensitively at 550 °C. In order to enhance the selectivity towards H₂, a selective C₃H₆ oxidation catalyst was employed to minimize unwanted responses caused by interfering gases. Among the examined metal oxides, Cr₂O₃ facilitated the selective oxidation of C₃H₆. However, the addition or lamination of Cr₂O₃ to SnO₂ (+30 wt.% YSZ)-SE was found to diminish the sensing responses to all examined gases. Therefore, an intermediate layer of Al₂O₃ was sandwiched between the SE layer and the catalyst layer to prevent the penetration of Cr₂O₃ particles into the SE layer. The sensor using SnO₂ (+30 wt.% YSZ)-SE coated with a catalyst layer of Cr₂O₃ as well as an intermediate layer of Al₂O₃ exhibited a sensitive response toward H₂, with only minor responses toward other examined gases at 550 °C under humid conditions (21 vol.% O₂ and 1.35 vol.% H₂O in N₂ balance). A linear relationship was observed between sensitivity and H₂ concentration in the range of 20–800 ppm on a logarithmic scale. The results of sensing performance evaluation and polarization curve measurements indicate that the sensing mechanism is based on the mixed-potential model.