Interfacial engineering of nickel/vanadium based two-dimensional layered double hydroxide for solid-state hydrogen storage in MgH2

As a high-density solid-state hydrogen storage material, magnesium hydride (MgH₂) is promising for hydrogen transportation and storage. Yet, its stable thermodynamics and sluggish kinetics are unfavorable for that required for commercial application. Herein, nickel/vanadium trioxide (Ni/V₂O₃) nanoparticles with heterostructures were successfully prepared via hydrogenating the NiV-based two-dimensional layered double hydroxide (NiV-LDH). MgH₂ + 7 wt% Ni/V₂O₃ presented more superior hydrogen absorption and desorption performances than pure MgH₂ and MgH₂ + 7 wt% NiV-LDH. The initial discharging temperature of MgH₂ was significantly reduced to 190 °C after adding 7 wt% Ni/V₂O₃, which was 22 and 128 °C lower than that of 7 wt% NiV-LDH modified MgH₂ and additive-free MgH₂, respectively. The completely dehydrogenated MgH₂ + 7 wt% Ni/V₂O₃ charged 5.25 wt% H₂ in 20 min at 125 °C, while the hydrogen absorption capacity of pure MgH₂ only amounted to 4.82 wt% H₂ at a higher temperature of 200 °C for a longer time of 60 min. Moreover, compared with MgH₂ + 7 wt% NiV-LDH, MgH₂ + 7 wt% Ni/V₂O₃ shows better cycling performance. The microstructure analysis indicated the heterostructural Ni/V₂O₃ nanoparticles were uniformly distributed. Mg₂Ni/Mg₂NiH₄ and metallic V were formed in-situ during cycling, which synergistically tuned the hydrogen storage process in MgH₂. Our work presents a facile interfacial engineering method to enhance the catalytic activity by constructing a heterostructure, which may provide the mentality of designing efficient catalysts for hydrogen storage.