Effects of Al2O3 addition on sintering behaviour,microstructure, and physical properties of Al2O3/vitrified bond CBN composite

The effects of Al₂O₃ content on the sintering behaviour, microstructure, and physical properties of Al₂O₃/vitrified bonds (SiO₂–Al₂O₃–B₂O₃–BaO–Na₂O–Li₂O–ZnO–MgO) and Al₂O₃/vitrified bond cubic boron nitride (CBN) composites were systematically investigated using X-ray diffraction, differential scanning calorimetry, dilatometry, scanning electron microscopy, and X-ray photoelectron spectroscopy. Various amounts of Al₂O₃ promoted the formation of BaAl₂Si₂O₈ and γ-LiAlSi₂O₆, increasing the relative crystallinity of the Al₂O₃/vitrified composite from 85.0 to 93.2%, resulting in residual compressive stress on BaAl₂Si₂O₈, thereby influencing the thermal behaviour and mechanical properties of the Al₂O₃/vitrified composite. The bulk density, porosity, flexural strength, hardness, and thermal conductivity of 57.5 wt% Al₂O₃ sintered at 950 °C were 3.12 g/cm³, 6.1%, 169 MPa, 90.5 HRC, and 4.17 W/(m·K), respectively. The coefficient of thermal expansion of the bonding material was 3.83 × 10^?6 °C^?1, which was comparable to that of CBN, and the number of N–Al bonds were increased, which boosted the flexural strength of the Al₂O₃/vitrified CBN composite to 81 MPa. The excellent mechanical properties, compact structure, and suitable interfacial bonding state with the CBN grains of the Al₂O₃/vitrified composite make it a promising high-performance bonding material for superhard abrasive tools.