Schäden wälzbeanspruchter DLC‐Schichten auf Stahlsubstraten unterschiedlicher Härte |
| |
Authors: | D. Spaltmann,M. Lö hr,S. Binkowski,N. Kelling,R. Soltwedel,M. Woydt,E. Santner |
| |
Abstract: | Damages of slip‐rolling tested DLC coatings on steel substrates of different hardness Extremely hard diamond coatings on hard SSiC substrates, various hard DLC coatings on 100Cr6 substrates (HRC60) as well as selected DLC coatings on unhardened steel substrates (HRC20) were tested under slip‐rolling conditions. Unadditivated paraffin oil was used as a lubricant. The tests were carried out in an Amsler type twin disc tester at initial maximum pressures of P0=2.3 GPa according to Hertz. The tests were terminated after n=1.000.000 revolutions (endurance tests: n=10.000.000 revolutions) or if a coherent damaged area of A>1 mm2 occurred. The slip‐rolling tests showed that the SSiC had a supportive influence on the diamond coatings which, however, failed due to fractures in the substrate. At least two of the DLC coatings on 100Cr6 substrates (HRC60) withstood the slip‐rolling test for up to n=10.000.000 revolutions with nearly no visible damage. These coatings deposited onto a soft, nitrogen alloyed steel (HRC20) were able to adjust to the deformation of the substrate without major damaged areas (A>1 mm2). |
| |
Keywords: | Wä lzen Schmierung Hä rte DLC Stahl Slip‐rolling lubrication hardness DLC steel |
|
|