Micro-structural and tensile strength analyses on the magnesium matrix composites reinforced with coated carbon fiber

Magnesium matrix composites reinforced with SiO₂ coated carbon fibers have been investigated, with an emphasis given on the relation between the material strength and interfacial microstructure. The composites were studied as a function of aluminium (Al) content that is varied between 0 and 9 wt%. The obtained results indicate that the reactivity at the C/Mg–Al interface of the composite can be controlled by varying the Al content. The low Al content in C/Mg–1Al has been completely dissolved in the matrix with no segregation even after solidification, leading to the best mechanical performance. If the Al content is increased to ≥3 wt% (composites such as C/AZ31 and C/AZ91), the SiO₂ coatings are fully depleted due to an extensive formation of carbides at the interface. The precipitates are further identified as Al₂MgC₂ phase that is similar to binary carbide Al₄C₃. SiO₂ coating on the fiber layer prior to fabrication of composite is found to be a promising way to suppress the carbide formation and enable the use of Mg–Al matrix with appropriate Al content.