Structural and surface properties of thermally prepared Ti/RhxTi(1−x)Oy electrodes: I—influence of preparation parameters |
| |
Authors: | P.M De CamposA.V Benedetti L.A De FariaV Cardoso J.F.C Boodts |
| |
Affiliation: | a Institute of Chemistry of São Carlos, University of São Paulo, Sao Carlos, SP, Brazil b Institute of Chemistry of Araraquara/UNESP, Araraquara, SP, Brazil c Institute of Chemistry, Federal University of Uberlândia, Uberlandia, MG, Brazil |
| |
Abstract: | Electrodes of RhxTi(1−x)Oy nominal composition were prepared by thermal decomposition of the chloride or nitrate precursor salts dissolved in strongly acidic medium and applied by brush to both sides of a Ti° support. A systematic study of the influence of calcination temperature and time as well as oxygen flux was conducted. The coatings were characterised by SEM, EDAX, XRD, open circuit potential measurements and cyclic voltammetry (CV). Visible-ultraviolet spectrophotometry was employed to identify the chemical form of the precursor in solution while thermogravimetric analysis (TGA) was used to assess the decomposition temperature ranges. Optimisation of the coating preparation parameters showed coatings obtained from [Rh(H2O)6](NO3)3 precursor dissolved in HNO3 1:2 (v/v) and fired at 430 °C for 2 h in a 5 l min−1 oxygen stream-furnished stable electrodes having the highest electrochemically active surface area. |
| |
Keywords: | Electrocatalysis Dimensionally stable anodes Rhodium oxide Optimisation Characterisation |
本文献已被 ScienceDirect 等数据库收录! |
|