In-situ fabrication of Al3V/Al2O3 nanocomposite through mechanochemical synthesis and evaluation of its mechanism

In this research, in situ fabrication of Al₃V based nanocomposite and its formation mechanism have been investigated. In order to synthesize Al₃V/Al₂O₃ nanocomposite, a mixture of Al and V₂O₅ powders was subjected to high-energy ball milling and the nanocomposite was produced through a mechanochemical reaction. The produced structure was isothermally heat-treated at 500–600 °C for 0.5–2 h under argon atmosphere. In order to evaluate the structural changes during milling and annealing, the synthesized powders were characterized by X-ray diffraction (XRD). Moreover, the powder morphological changes were studied by scanning electron microscopy (SEM). It was observed that the reaction between Al and V₂O₅ occurred after about 30 min and, the Al₃V and Al₂O₃ were formed in nanocrystalline structure with the continuing mechanical milling. Calculation of adiabatic temperature confirmed that reaction took place in combustion mode. In final stage of milling up to 40 h; it was observed that the Al₃V decomposed to Al and V so that the optimum time of milling to achieve fabrication of nanocomposite was determined to be about 20 h. Calculations based on Miedema’s model verified partial disordering of Al₃V during further milling and annealing of as-milled powder at 600 °C led to the ordering of Al₃V. The crystallite size of Al₃V and Al₂O₃ after annealing at 600 °C for 2 h remained in nanometer scale. So the final product appeared to be stable even after annealing.