Influence of SrTiO3 modification on dielectric properties of Mg(Zr0.05Ti0.95)O3 ceramics at microwave frequency

The microwave dielectric properties and microstructures were investigated in the (1?x)Mg(Zr_0.05Ti_0.95)O₃–xSrTiO₃ (hereafter referred to as (1?x)MZT–xST) system. The compounds were prepared via the conventional solid-state reaction. Compositions in the (1?x)Mg(Zr_0.05Ti_0.95)O₃–xSrTiO₃ system were designed to compensate the negative temperature coefficient of the resonant frequency of Mg(Zr_0.05Ti_0.95)O₃. The values displayed nonmonotonic mixture-like behavior, because the TiO₂ phase was formed in the MZT composite ceramics with increasing x. A close zero τ_f of 0.2 ppm/°C could be achieved at 0.96MZT–0.04ST with ?_r = 20.8 and Q × f = 257,000 GHz.