New PEEK-WC and PLA membranes for H2 separation

The potentialities of PEEK-WC (thermally treated at 120 °C) and PLA polymers have been studied in the field of membrane technology applied to H₂ separation/purification. In particular, for low/medium temperature operation (80 °C), PEEK-WC membranes (66 μm thick) showed good results in terms of H₂/CH₄ separation, showing an ideal selectivity value higher than 40. Meanwhile, we observed interesting selectivity also for H₂/N₂ and H₂/CO₂ separation, reaching values of 24 and 20, respectively. As expected, for PEEK-WC thermally treated membranes, the H₂ permeating flux increased from 25 to 80 °C and by increasing the transmembrane pressure. Furthermore, H₂ permeability at 80 °C was around 20 barrer. Concerning PLA membranes (26 μm thick), it is worth of noting that this polymer was pioneeristically used in this work as membrane application, showing great results in terms of H₂/CO₂ separation. Indeed, we overcame the Robeson's upper-bound (2008), achieving an ideal selectivity H₂/CO₂ around 25 with an H₂ permeability of 25 barrer. Further advantage due to the utilization of PLA membranes was related to the temperature operations set at ambient conditions, constituting a valuable and cost-effective solution for H₂/CO₂ separation processes via polymeric membrane technology.