Proton Conductivity in Zr4+-Ion-Doped P2O5–SiO2 Porous Glasses

The effect of zirconium ions on glass structure and proton conductivity was investigated for sol-gel-derived P₂O₅–SiO₂ glasses. Porous glasses were prepared through hydrolysis of PO(OCH₃)₃, Zr(OC₄H₉)₄, and Si(OC₂H₅)₄. Chemical bonding of the P⁵⁺ ions was characterized using ³¹P-NMR spectra. The phosphorous ions, occurring as PO(OH)₃ in the ZrO₂-free glass, were polymerized with one or two bridging oxygen ions per PO₄ unit with increased ZrO₂ content. The chemical stability of these glasses was increased significantly on the addition of ZrO₂, but the conductivity gradually decreased from 26 to 12 mS/cm at room temperature for 10P₂O₅·7ZrO₂·83SiO₂ glass. A fuel cell was constructed using 10P₂O₅·5ZrO₂·85SiO₂ glass as the electrolyte; a power of ∼4.5 mW/cm² was attained.