Fabrication of cast carbon steel with ultrafine TiC particles

The carbon steels dispersed with ultrafine TiC particles were fabricated by conventional casting method. The casting process is more economical than other available routes for metal matrix composite production, and the large sized components to be fabricated in short processing time. However, it is extremely difficult to obtain uniform dispersion of ultrafine ceramic particles in liquid metals due to the poor wettability and the specific gravity difference between the ceramic particle and metal matrix. In order to solve these problems, the mechanical milling (MM) and surface-active processes were introduced. As a result, Cu coated ultrafine TiC powders made by MM process using high energy ball milling machine were mixed with Sn powders as a surfactant to get better wettability by lowering the surface tension of carbon steel melt. The microstructural investigations by OM show that ultrafine TiC particles are distributed uniformly in carbon steel matrix. The grain sizes of the cast matrix with ultrafine TiC particles are much smaller than those without ultrafine TiC particles. This is probably due to the fact that TiC particles act as nucleation sites during solidification. The wear resistance of cast carbon steel composites added with MMed TiC/Cu-Sn powders is improved due to grain size refinement.