Epitaxial SrRuO3 thin films deposited on SrO buffered-Si(001) substrates for ferroelectric Pb(Zr0.2Ti0.8)O3 thin films

SrRuO₃ thin film electrodes are epitaxially grown on SrO buffered-Si(001) substrates by pulsed laser deposition. The optimum conditions of the SrO buffer layers for epitaxial SrRuO₃ films are a deposition temperature of 700 °C, deposition pressure of 1 × 10^?6 Torr, and thickness of 6 nm. The 100 nm thick-SrRuO₃ bottom electrodes deposited above 650 °C on SrO buffered-Si (001) substrates have a rms (root mean square) roughness of approximately 5.0 Å and a resistivity of 1700 µω-cm, exhibiting an epitaxial relationship. The 100 nm thick-Pb(Zr_0.2Ti_0.8)O₃ thin films deposited at 575 °C have a (00l) preferred orientation and exhibit 2P_r of 40 µC/cm², E_c of 100 kV/cm, and leakage current of about 1 × 10^?7 A/cm² at 1 V. The silicon oxide phase which presents within PZT and SrRuO₃ films, influences the crystallinity of the PZT films and the resistivity of the SrRuO₃ electrodes.