Preparation of Tortuous 3D γ‐CsPbI3 Films at Low Temperature by CaI2 as Dopant for Highly Efficient Perovskite Solar Cells

Inorganic cubic CsPbI₃ perovskite (α‐CsPbI₃) has been widely explored for perovskite solar cells (PSCs) due to its thermal stability and suitable bandgap of 1.73 eV. However, α‐CsPbI₃ usually requires high synthesis temperatures (>320 °C). Additionally, it usually undergoes phase transition to the nonperovskite structure phase (β‐CsPbI₃), which results in poor photoelectric performance in devices. In this study, it is first found that the tortuous 3D CsPbI₃ phase (γ‐CsPbI₃) can be prepared and used for PSCs by solution process without any additive at low temperature (60 °C). The γ‐CsPbI₃ exhibits suitable bandgap of 1.75 eV and favorable photoelectric properties. However, γ‐CsPbI₃ is a metastable phase and easily transforms into β‐CsPbI₃ in ambient moisture. In order to improve the stability of γ‐CsPbI₃, calcium ions (Ca²⁺) with a relatively small radius of 100 pm are used to partially substitute lead ions (119 pm). This research proves that Ca²⁺ can effectively improve the stability of the γ‐CsPbI₃ at room temperature. By optimizing the doping concentration of Ca²⁺ (CsPb_1?xCa_xI₃, x is from 0% to 2%), the Ca²⁺‐doped γ‐CsPbI₃ PSCs achieve a hysteresis‐free J–V curve and a maximum power conversion efficiency (PCE) of 9.20%.