Effects of Gd3+ substitution on the structure,photoluminescence, scintillation,and thermometric features of Pr3+:Lu2Zr2O7 phosphors

In this study, it is shown how the photoluminescence, scintillation, and optical thermometric properties are managed via the introduction of Gd³⁺ ions into Pr³⁺:Lu₂Zr₂O₇. Raman spectra validate that partial replacement of Lu³⁺ with Gd³⁺ can promote the phase transition of Lu₂Zr₂O₇ host from the defective fluorite structure to the ordered pyrochlore one. Upon 289 nm excitation, all the samples emit the 483 (³P₀ → ³H₄), 581 (¹D₂ → ³H₄), 611 (³P₀ → ³H₆), 636 (³P₀ → ³F₂), and 714 nm (³P₀ → ³F₄) emissions from Pr³⁺ ions, which are enhanced with the addition of Gd³⁺ ions due to the modification of crystal structure. Dissimilarly, the X-ray excited luminescence spectra consist of a strong emission located at 314 nm from Gd³⁺ ions (⁶P_7/2 → ⁸S_7/2), together with the typical emissions from Pr³⁺ ions, which exhibit different dependences on the Gd³⁺ concentration. When the luminescence intensity ratio between the ³P₀ → ³H₆ (611 nm) and ¹D₂ → ³H₄ (581 nm) transitions is selected for temperature sensing, Pr³⁺:(Lu_0.75Gd_0.25)₂Zr₂O₇ shows the optimal relative sensing sensitivity of 0.78% K^?1 at 303 K, which is higher than that of the Gd³⁺-free sample. Therefore, the developed Pr³⁺:(Lu, Gd)₂Zr₂O₇ phosphors have the applicative potential for optical thermometry, X-ray detection, and photodynamic therapy.