Magneto-optical,thermal, and mechanical properties of polycrystalline Tb3Al5O12 transparent ceramics

Terbium aluminum garnet (Tb₃Al₅O₁₂, TAG) ceramics have become a promising magneto-optical material owing to the outstanding comprehensive performance, including the magneto-optical, thermal, and mechanical properties. Fine-grained TAG ceramics with high optical quality and mechanical properties have attracted much attention. In this study, TAG ceramics with fine grains and high optical quality are fabricated successfully by a two-step sintering method from co-precipitated nano-powders. After pre-sintered at 1525°C in vacuum and hot isostatic pressed at 1600°C, the in-line transmittance of TAG ceramics reaches 81.8% at 1064 nm, and the average grain size is 7.1 μm. The Verdet constant of TAG ceramics is −179.6 ± 4.8 rad T⁻¹ m⁻¹ at 633 nm and −52.1 ± 1.9 rad T⁻¹ m⁻¹ at 1064 nm, higher than that of commercial Tb₃Ga₅O₁₂ crystals. The thermal conductivity of TAG ceramics is determined from 25 to 450°C, and the result is 5.12 W m⁻¹ K⁻¹ at 25°C and 3.61 W m⁻¹ K⁻¹ at 450°C. A comparison of mechanical properties between large- and fine-grained TAG ceramics fabricated under different conditions is conducted. The fine-grained TAG ceramics possess a bending strength of 226.3 ± 16.4 MPa, which is 9.7% higher than that of the large-grained ceramics. These results indicate that reducing the grain size on the premise of high optical quality helps improve the comprehensive performance of TAG ceramics.