Entwicklung von Oxid – Keramik zur Anwendung als Wärmedämmschichten

Development of Oxide Ceramics for an Application as TBC The standard thermal barrier coating material yttria stabilised zirconia (YSZ) is limited in long term operation to a maximum temperature of about 1200°C. As a result further increase of the gas inlet temperature and hence the efficiency of gas turbines are hardly to achieve with YSZ coatings. In a screening procedure especially perowskite (ABO₃, A = Sr,Ba, B = Zr) and pyrochlore (A₂B₂O₇, e.g. A = La and other rare earth elements, B = e.g. Zr) materials have been identified as possible candidates for thermal barrier coatings. Basic physical properties (e.g. thermal expansion coefficient, thermal diffusivity and conductivity) of several candidates have been determined using sintered, dense samples. The possibility of optimization of the properties by using specific compositions will be discussed. From promising materials powders which are suitable for plasma‐spraying have been produced by spray‐drying. New TBC systems consisting of new materials (BaZrO₃, La₂Zr₂O₇) deposited by atmospheric plasma spraying and vacuum plasma sprayed MCrAlY bondcoats were tested in a gas burner facility. Especially La₂Zr₂O₇ coatings gave promising results. A further improvements could be achieved by the use of layered or graded coatings with a YSZ coating at the bondcoat interface and on top a layer of the new TBC material. First results of thermal cycling tests with 1250 and 1350°C surface temperature will be presented.