Hydrogen production from water splitting over Eosin Y-sensitized mesoporous-assembled perovskite titanate nanocrystal photocatalysts under visible light irradiation |
| |
Authors: | Tarawipa Puangpetch Pichayaon Sommakettarin Sumaeth Chavadej Thammanoon Sreethawong |
| |
Affiliation: | 1. Department of Chemical Engineering, Faculty of Engineering and Industrial Technology, Silpakorn University, Nakhon Pathom 73000, Thailand;2. The Petroleum and Petrochemical College, Chulalongkorn University, Soi Chula 12, Phyathai Road, Pathumwan, Bangkok 10330, Thailand;3. Center for Petroleum, Petrochemicals, and Advanced Materials, Chulalongkorn University, Bangkok 10330, Thailand |
| |
Abstract: | The photocatalytic water splitting is a promising process for producing H2 from two abundant renewable sources of water and solar light, with the aid of a suitable photocatalyst. In this work, a combination of sensitizer addition and noble metal loading was employed to modify perovskite photocatalysts in order to achieve the enhancement of photocatalytic H2 production under visible light irradiation. The dependence of the H2 production on type of mesoporous-assembled perovskite titanate nanocrystal photocatalysts (MgTiO3, CaTiO3, and SrTiO3), calcination temperature of photocatalyst, Pt loading, type and concentration of electron donor (diethanolamine, DEA; and triethanolamine, TEA), concentration of sensitizer (Eosin Y, E.Y.), photocatalyst dosage, and initial solution pH, was systematically studied. The experimental results showed that the 0.5 wt.% Pt-loaded mesoporous-assembled SrTiO3 nanocrystal synthesized by a single-step sol-gel method and calcined at 650 °C exhibited the highest photocatalytic H2 production activity from a 15 vol% DEA aqueous solution with dissolved 0.5 mM E.Y. Moreover, the optimum photocatalyst dosage and initial solution pH for the maximum photocatalytic H2 production activity were found to be 6 g/l and 11.6, respectively. |
| |
Keywords: | Hydrogen production Water splitting Visible light Sensitization Perovskite titanate |
本文献已被 ScienceDirect 等数据库收录! |
|