透明裂纹釉影响因素的探究 |
| |
引用本文: | 洪琛,沈华荣,徐强,卢希龙,曹春娥.透明裂纹釉影响因素的探究[J].中国陶瓷工业,2014(4):15-20. |
| |
作者姓名: | 洪琛 沈华荣 徐强 卢希龙 曹春娥 |
| |
作者单位: | 景德镇陶瓷学院,江西景德镇333001 |
| |
摘 要: | 本项目以较好的透明裂纹釉配方为基础,考察其釉料组成、工艺参数和烧成制度等对釉面效果的影响。实验结果证明:较好的组成范围是,钠长石为70-78wt.%,高岭土1-3wt.%,石英12-20wt.%,石灰石6-12wt.%;烧成温度为1290℃,保温30 min,冷却速度20℃/min;釉层厚度为0.8~1.3 mm,球磨时间是20 min。所得样品釉面光滑平整、透明度较好,裂纹也具有较好艺术效果。
|
关 键 词: | 透明釉 裂纹釉 釉面效果 影响因素 |
Factors Inlfuencing Transparent Crackle Glaze |
| |
Affiliation: | HONG Chen, SHEN Huarong, XU Qiang, LU Xilong, CAO Chun’e (Jingdezhen Ceramic Institute, Jingdezhen, 333001 Jiangxi, China) |
| |
Abstract: | The effects of glaze composition, process parameters and firing systems on glaze result were studied for a better formula of transparent crackle glaze. Experimental results show that the preferable range of the composition is sodium feldspar 70 ~ 78 wt%, kaolin 1 ~ 3 wt%, quartz 12 ~ 20 wt%, limestone 6 ~ 12 wt%; ifring temperature is 1290℃, holding time is 30min, cooling rate is 20 ℃/min; glaze layer thickness is 0.8 ~ 1.3 mm, and the milling time is 20min. The glaze surface of the resulted samples was smooth with better transparency and artistic crackle effect. |
| |
Keywords: | transparent glaze crackle glaze glaze effect inlfuencing factors |