| Abstract: | The aim of this study was to investigate the effect of heat‐treated lignocellulosic filler on the surface characteristics and decay resistance of the wood flour/styrene maleic anhydride (SMA) composites. In this study, heat treatment was conducted at 212°C for 8 hours. Test specimens were prepared by injection molding at 220°C. Weathering tests were performed by cycles of UV‐light irradiation for 8 hours, water spray for 15 minutes, and then conditioning for 3.45 hours in an accelerated weathering test cycle chamber. Heat‐treated wood flour/SMA composites were evaluated for color changes, and attenuated total reflectance Fourier transform infrared (FTIR) spectroscopy was used to analyze chemical changes on the sample surfaces. The wood decay tests were performed of white rot fungus, Trametes versicolor (L.: Fr.) Pilat was based on mini‐block specimens on 48% malt extract agar in petri dishes. The study showed that color changes occurred when heat‐treated filler rate is increased in this material. Therefore, materials in 10% filler rate show lower color changes than other variation. As a result of the FTIR analysis, the addition of wood filler into the SMA causes changes in the chemical structure. In addition, the increase in wood filler reduced the resistance to weathering. Decay results showed that thermally modified wood has lower mass loss caused by fungal attack than untreated wood material. The weight loss decreases with the increase in wood flour rate expect 10%T and 10%UT in all composites. |