Effect of annealing and quenching on superconductivity in Pb and Sb-doped Bi2Sr2Ca2Cu3O x

Samples of the series Bi_1·9−x Pb _x Sb_0·1Sr₂Ca₂Cu₃O _y withx=0, 0·1, 0·2, 0·3 and 0·4 were prepared by the solid-state route. The X-ray and d.c. electrical resistivity data on furnace-cooled and quenched samples are presented. Though the starting composition is 2223, the end products were multiphase with 4334 as the major phase. A superconducting transition withT _c=100K was observed in the pure 2223 sample after quenching. The furnace-cooled samples were metallic, while samples withx=0·1, 0·2 and 0·3 were superconducting after quenching. The amount of the 4334 phase decreases with increasing Pb content. Quenching seems to be favourable for the formation of the 4334 phase.