Electrochemical Characteristics in Seawater for Cold Thermal Spray-Coated Al-Mg Alloy Layer |
| |
Authors: | Il-Cho Park Seong-Jong Kim |
| |
Affiliation: | Division of Marine Engineering, Mokpo National Maritime University, 91, Haeyangdaehak-ro, Mokpo-si, Jeollanam-do 58628, Korea |
| |
Abstract: | For corrosion protection of carbon steel in a marine environment,cold arc thermal spray coating was applied to the surface with Al and Al-Mg alloy wires.The surface hardness of Al and Al-Mg thermal spray coatings increased with Mg content.And the various electrochemical experiments were carried out to evaluate corrosion damage characteristics of the thermal spray coating layers.The Al and Al-Mg thermal spray coating layers presented negative potentials compared to carbon steel in corrosion potential measurements.And an anodic polarization experiment revealed a tendency of activation polarization with no passivation.Furthermore,the corrosion damage of the thermal spray coating layer in galvanostatic experiment was observed mainly at the defect area,and the Al-3Mg thermal spray coating layer presented less surface damages than others.In addition,the Al-3Mg thermal spray coating layer showed the lowest corrosion rate while having a sufficient driving voltage for cathodic corrosion protection.Therefore,it is an optimal thermal spray material for sacrificial anode. |
| |
Keywords: | Corrosion protection Carbon steel Arc thermal spray coating Al-Mg alloy Marine environment |
本文献已被 CNKI 等数据库收录! |
| 点击此处可从《金属学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《金属学报(英文版)》下载全文 |
|