Hot deformation of spray formed nickel-base superalloy using processing maps |
| |
Authors: | KANG Fu-wei ZHANG Guo-qing LI Zhou SUN Jian-fei |
| |
Affiliation: | [1]School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China [2]School of Materials Science and Engineering, Harbin University of Science and Technology, Harbin 150040, China [3]Beijing Institute of Aeronautical Materials, Beijing 100095, China |
| |
Abstract: | The hot compression testing of hot isostatically pressed (HIPed) spray formed (SF) nickel-base superalloy was carried out by thermal mechanical simulator in the temperature range of 1050-1140℃ at strain rates of 0.01-10 S-1 and engineering strain of 50%. A processing map was developed on the basis of these data by using the principles of dynamic materials modeling. The microstructural evolution of deformed samples was also examined on the basis of optical and electron microscopic observations. The map exhibits two domains: the instability domain at the temperatures of 1050℃-1110℃ and strain rate of 0.01 S-1, the stability domain at the temperatures of 1110℃-1140℃ and strain rates of 1s-1-10 S-1, with a peak efficiency of about 40%. The dynamic recrystallization(DRX) is observed in the stability domain and the deformed specimens are no cracking or instabilities. However, there is no DRX in the instability domain and the alloy exhibits flow instability with cracks due to poor workability. The optimum hot working condition Was determined in the stability domain. |
| |
Keywords: | spray forming nickel-base superalloy hot compression processing map recrystallization |
本文献已被 维普 万方数据 等数据库收录! |
|