Oxidation Performance and Interdiffusion Behavior of a Pt-Modified Aluminide Coating with Pre-deposition of Ni |
| |
Authors: | He Liu Shuai Li Cheng-Yang Jiang Chun-Tang Yu Ze-Bin Bao Sheng-Long Zhu Fu-Hui Wang |
| |
Affiliation: | 1. Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China;2. School of Materials Science and Engineering, University of Science and Technology of China, Shenyang 110016, China;3. Shenyang National Laboratory for Materials Science,Northeastern University, Shenyang 110819, China |
| |
Abstract: | To refrain the interdiffusion of elements while holding good oxidation resistance, a (Ni,Pt)Al/Ni composite coating was prepared by sequential treatments of electroplating Ni and Pt and successive gaseous aluminization. In comparison with normal (Ni,Pt)Al coating, high-temperature performance of the composite coating was evaluated in isothermal oxidation test at 1100 °C. Both the two coatings exhibited good resistance against high-temperature oxidation, but the interdiffusion of elements between composite coating and single-crystal (SC) superalloy substrate was greatly relieved, in which the thickness of secondary reaction zone (SRZ) and the amount of precipitated topologically close-packed phase in the SC alloy matrix were significantly decreased. Mechanisms responsible for delaying rate of coating degradation and SRZ growth/propagation are discussed. |
| |
Keywords: | Aluminide coating Oxidation Interdiffusion Microstructure |
本文献已被 CNKI 等数据库收录! |
| 点击此处可从《金属学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《金属学报(英文版)》下载全文 |
|