Influence of Pin Offset on Microstructure and Mechanical Properties of Friction Stir Welded Mg/Ti Dissimilar Alloys |
| |
Authors: | Qi Song Zhong-Wei Ma Shu-De Ji Qing-Hua Li Liu-Fang Wang Rui Li |
| |
Affiliation: | 1. School of Aerospace Engineering, Shenyang Aerospace University, Shenyang 110136, China |
| |
Abstract: | The influences of pin offset on the formation, microstructure and mechanical properties of friction stir welded joint of Ti6Al4V and AZ31B Mg dissimilar alloys were investigated. The results show that sound joints are obtained at different offsets. With the offset decreasing from 2.5 to 2.1 mm, the number of Ti alloy fragments is increased, and the stir zone (SZ) is enlarged and the grains in SZ become coarser. A hook-like structure is formed at the Mg/Ti interface and its length is increased with the decrease in pin offset. The Al element has an enrichment trend at the Ti alloy side near the Mg/Ti interface when the offset is decreased, which is beneficial to the bonding of the interface. An Al-rich layer with a thickness of 3-5 μm forms at the offset of 2.1 mm. All the joints fracture at the interface and present a mixed ductile-and-brittle fracture mode. The joint tensile strength is increased with the offset decreasing from 2.5 to 2.1 mm, and the maximum tensile strength of 175 MPa is acquired at the offset of 2.1 mm. |
| |
Keywords: | Mg/Ti dissimilar alloys Friction stir welding Pin offset Mechanical properties Microstructure |
本文献已被 CNKI 万方数据 等数据库收录! |
| 点击此处可从《金属学报(英文版)》浏览原始摘要信息 |
|
点击此处可从《金属学报(英文版)》下载全文 |