Nanocrystallites-forming hierarchical porous Ni/Al2O3–TiO2 catalyst for dehydrogenation of organic chemical hydrides

Dehydrogenation of organic chemical hydrides has been improved by reconstructing the catalyst in the form of hierarchical porous structure nanocatalyst, in which the economical Ni was adopted as catalytic component and nano Al₂O₃–TiO₂ hybrid composite as support. The Al₂O₃–TiO₂ composite was prepared by spontaneous self-assembly of nano Al₂O₃ and TiO₂ aggregates by hydrolysis of tetra-n-butyl-titanate under continuous agitation. The multi-scaled distribution of Al₂O₃–TiO₂ aggregates with hierarchy could be observed in dynamic light scattering spectrometer. The aggregates are comprised of nano-sized γ-Al₂O₃ and anatase TiO₂ crystallites with sizes of about 5 and 7 nm, respectively. The surface modulation by TiO₂ could be verified in FTIR Spectra. The migration of Ti species and crystallite growth were hindered by the Al₂O₃ skeleton and the hierarchical porous structure was sustained during the thermal related process. The multi-scaled distributed pores were confirmed by both TEM analysis and N₂ adsorption results. The results of dehydrogenation experiments showed that the hierarchical porous structure nano Ni/Al₂O₃–TiO₂ exhibited superior catalytic performance to Ni/Al₂O₃ with the optimum conversion of 99.9% at 400 °C, while the catalyst of Ni/Al₂O₃ exhibited only 16.5% under the same condition.