Low-Temperature Synthesis of Calcium Hexa-Aluminate

Calcium hexa-aluminate (CaO·6Al₂O₃) has been prepared from calcium nitrate and aluminum sulfate solutions in the temperature range of 1000°–1400°C. A 0.3 mol/L solution of aluminum sulfate was prepared, and calcium nitrate was dissolved in it in a ratio that produced 6 mol of Al₂(SO₄)₃·16H₂O for each mole of Ca(NO₃)₂·4H₂O. It was dried over a hot magnetic stirrer at ～70°C and fired at 1000°–1400°C for 30–360 min. The phases formed were determined by XRD. It was observed that CaO·Al₂O₃ and CaO·2Al₂O₃ were also formed as reaction intermediates in the reaction mix of CaO·6Al₂O₃. The kinetics of the formation of CaO·6Al₂O₃ have been studied using the phase-boundary-controlled equation 1 ? (1 ? x )^1/3= K log t and the Arrhenius plot. The activation energy for the low-temperature synthesis of CaO·6Al₂O₃ was 40 kJ/mol.